Product details
Product manual
Filler/reinforced material Glass fiber reinforced material, 30% filler
General description
Material status
Solid state
Exterior
natural color
processing methods
Injection molding
Stuffing
glass fiber
form
particle
Physical properties [1]
Test method
Test Conditions
Unit
Attribute value[2]
proportion
ASTM D792
(23±0.5)°C
g/cm3
1.120
Melt mass flow rate
ASTM D1238
230°C/2.16kg
g/10min
2.54
Shrinkage
ASTM D955
%
0.3
Mechanical properties [1]
Test method
Test Conditions
Unit
Attribute value[2]
Tensile Strength
ASTM D638
50mm/min
MPa
55.8
Bending strength
ASTM D790
2mm/min
MPa
82.7
Flexural modulus
ASTM D790
2mm/min
MPa
4830
Thermal performance [1]
Test method
Test Conditions
Unit
Attribute value[2]
Heat distortion temperature
ASTM D648
0.45MPa,Unannealed
°C
154
Impact performance [1]
Test method
Test Conditions
Unit
Attribute value[2]
Izod notched impact strength
ASTM D256
(23±3)°C
J/m
53
Flammability [1]
Test method
Test Conditions
Unit
Attribute value[2]
UL flame retardant rating
UL 94
/
/
HB
[1] The material properties of different colors will vary.
[2] The attribute values are for reference only, not as any technical indicators or technical agreements.
PP-GF30 refers to glass fiber reinforced PP with an addition ratio of 30%. GF is the abbreviation of glass fiber and refers to glass fiber, which is a commonly used inorganic filler for modified plastics.
Glass fiber has the properties of high tensile strength, high impact energy absorption, elastic coefficient, good heat resistance, and low price. It is often used as a reinforcing phase to produce polymer, rubber and other composite materials. With its advantages of low cost, low density, corrosion resistance, stable processing and chemical properties, and recyclability, PP has become one of the most widely used general-purpose plastics in the world. Its application involves various fields of production and life. However, it has high shrinkage, easy cracking at low temperature, poor rigidity and impact performance, etc., which limit its application in some occasions. Therefore, glass fiber can be used to strengthen it, thereby reducing cost and optimizing mechanical properties.